Loctite®
97443

Loctite® Fixmaster® 235613 EA 3476 2-Part Stainless Steel Putty, 1 lb Tub, Paste Form, Dark/Blue/Gray Part A, Gray Part B, Part A: 1.57/Part B: 3.832

  • Manufacturer: Henkel
  • Brand: Loctite®
  • BSC Item#: 97443 LOCT
  • MPN: 235613
  • UPC: 079340974432
  • Min. Order Qty: 1
  • Qty. Interval: 1
  • Availability: Call for Availability

Loctite® Fixmaster® Stainless Steel Putty, 2-Part, Series: EA 3476, Tub Container, 1 lb Container, Epoxy Base, Composition: Part A: Calcium Carbonate, Epoxy Polyamine Adduct, Amine Adduct, Triethylenetetramine, Diethylenetriamine Silica Filler, Nonylphenol, Titanium Dioxide, 4-Methylimidazole, Part B: Epoxy Resin Chromium, Nickel, Molybdenum, Paste Form, 232 sq-cm at 6 mm THK/0.45 kg Coverage, 20 min Application Time, 6 hr Curing, Dark/Blue/Gray Part A, Gray Part B, Part A: Amine, Part B: Mild Odor/Scent, 30 to 105 deg C, Part A: 1.57/Part B: 3.832 Specific Gravity, Part A: > 93 deg C, Part B: 149 deg C Flash Point, 4:1, 9:1 Mixing Ratio, <10 g/L VOC, Applicable Materials: Steel, Cast Iron, Stainless Steel, Concrete, Wood, Clean, Abraded Bronze, Copper, Aluminum, 4600 psi Tensile Strength, 1800 psi Shear Strength

Type      :      2-Part
Series      :      EA 3476
Container Type      :      Tub
Container Size      :      1 lb
Base Type      :      Epoxy
Composition      :      Part A: Calcium Carbonate, Epoxy Polyamine Adduct, Amine Adduct, Triethylenetetramine, Diethylenetriamine Silica Filler, Nonylphenol, Titanium Dioxide, 4-Methylimidazole, Part B: Epoxy Resin Chromium, Nickel, Molybdenum
Form      :      Paste
Coverage      :      232 sq-cm at 6 mm THK/0.45 kg
Application Time      :      20 min
Curing Time      :      6 hr
Color      :      Dark/Blue/Gray Part A, Gray Part B
Odor/Scent      :      Part A: Amine, Part B: Mild
Temperature Rating      :      30 to 105 deg C
Specific Gravity      :      Part A: 1.57/Part B: 3.832
Flash Point      :      Part A: > 93 deg C, Part B: 149 deg C
Mixing Ratio      :      4:1, 9:1
VOC Content      :      <10 g/L
Applicable Materials      :      Steel, Cast Iron, Stainless Steel, Concrete, Wood, Clean, Abraded Bronze, Copper, Aluminum
Tensile Strength      :      4600 psi
Shear Strength      :      1800 psi
  • Resists rust and corrosion for long lasting repairs
  • Rebuilds worn parts fast limits downtime
  • High stainless steel content for durability
  • Superior adhesion forms a solid bond
  • Non-sag putty allows application versatility by conforming to unusual shapes
  • D 85 shore hardness
  • 40 to 50 min gel time 25 deg C
  • Epoxy hardener part A, epoxy resin part B
  • pdfSDS https://www.bsc-ind.com//ASSETS/DOCUMENTS/ITEMS/EN/Loctite_97443_SDS_1.pdf